HDPE Granules

HDPE Granules

Product Number: HDPE PN049,HDPE-100,HDPE-80,HDPE-6081H,HDPE-3000JE,HDPE-32F,HDPE-B507,HDPE-B502,HDPE-XP9020,HDPE-6098,etc.

Description:

HDPE is a highly crystalline non-polar thermoplastic resin produced through the copolymerization of ethylene and a small amount of α-olefin monomer. HDPE is synthesized under low pressure and is therefore also called low-pressure polyethylene. HDPE is mainly a linear molecular structure and has little branching. It has a high degree of crystallization and high density. It can withstand high temperatures and has good rigidity and mechanical strength and anti-chemical corrosion.

Applications:

HDPE is suitable for many plastic molding methods. Blow molding can be used for making various types of bottles, cans and industrial tanks and barrels. Injection molding is used for making various containers and goods of daily use, such as basins, barrels and baskets and furniture. Extrusion molding is used for making pipes, strapping tapes, fibers and single filaments and can also be used for making wires & cables covering materials and synthetic paper. After a large amount of inorganic filler is added, HDPE can also be used as an alternative to timber and cardboards for making calcium plastic packing containers, furniture, doors and windows.

Packaging:

25kg/bag

Description

Technical Parameter

Grades	HDPE PN049	HDPE-100	HDPE-80	HDPE-6081H	HDPE-3000JE	HDPE-32F	HDPE-B507	HDPE-B502	HDPE-XP9020	HDPE-6098
(5.0kg,190℃)Melt mass-flow rate,g/10min	0.26	0.26	0.430	6.22	2.2	1.98	6.43	1.86	0.14	0.38
Density,g/cm³	0.95	0.950	0.9458	0.9577	0.956	0.9373	0.948	0.9507	0.941	0.9494
Tensile stress at yield,Mpa	23.3	23.3	21.3	26.1	24.8	16.8	21.7	23.6	220	22.5
Modulus of elasticity in tension,Mpa	882	882	-	-	-	-	-	969	-	-
Flexural modulus,Mpa	1047	1047	955	1057	1020	741	-	-	6200	-
23℃ Charpy impact strength,KJ/m²	37.8	37.8	11.8H	4.2	12	28.6P	-	43.1P	-	-
Temperature of deflection under load(Tf0.45),℃	77	77	-	-	68	127.2	-	-	-	-
Water content,mg/kg	14	14	58	-	-	22	-	-	-	-
Volatile content,mg/kg	213	213	112	-	-	-	-	-	-	-
0xidation induction time(0IT,210℃),min	78.3	78.3	28.9	-	-	65.7	-	-	-	-
Nominal tensile strain at break,%	560	560	298	661	9.6	869	850	774	>600	466
Application	drain pipe	drain pipe	Water pipe	Injection bottle cap	Injection bottle cap	PEX-A floor heating pipe	various types of bottles, cans and industrial tanks and barrels	various types of bottles, cans and industrial tanks and barrels	Floor heating pipe	Shopping bag,market bag,garbage bag,drain pipe,etc.

Grades	HDPE-TR400N	HDPE-YEC-5505T	HDPE-5000S	HDPE-1158	HD6007XA	HDPE-QHJ01
(5.0kg,190℃)Melt mass-flow rate,g/10min	11.6(21.6kg)	0.7	1.0	2.1	0.6	0.7
Density,g/cm³	0.939	0.945	0.951	0.953	0.962	0.945
Tensile stress at yield,Mpa	20	19	25	24	30.5	18
Flexural modulus,Mpa	-	-	-	-	1700	9
23℃ Charpy impact strength,KJ/m²	-	-	-	32	-	-
Nominal tensile strain at break,%	799	500	800	600	300	500
Application	blow molding geomembrane products	communication cable jacket through fast-extrusion methods	package film, nets, ropes and small and medium-sized containers	Blow Molding Grade	Blow Molding Grade	Cable and wire